Beilstein J. Nanotechnol.2019,10, 1726–1736, doi:10.3762/bjnano.10.168
capacity of 843.4 mAh g−1, which corresponds to a capacity retention of 76.48% at a current rate of 0.2 C. Moreover, the Li/S battery with the TiO2/GO-coated separator showed superior cyclic performance and excellent rate capability, which shows the promise of the TiO2/GOcomposite in next-generation Li/S
batteries.
Keywords: dealloying; functional separator; lithium–sulfur batteries; TiO2/GOcomposite; Introduction
The portability of handheld electronic products and successful realization of next-generation electric vehicles urgently require advanced energy storage devices with higher storage capacity and
/GO-coated separator was introduced between the Li anode and sulfur cathode as a highly efficient polysulfide absorber. The TiO2/GOcomposite was prepared by dealloying, as reported elsewhere [35], and subsequent spray drying. It has been demonstrated that the utilization of the TiO2/GOcomposite
PDF
Figure 1:
Schematic illustration of a Li/S battery with a TiO2/GO-coated functional separator.